The belt carcass of this products is EP fabric ( D.S. EP or CC56 ) of high modulus, low shrink and high breaking tensile strength. Cover rubber of this product uses SBR, CR, EPDM rubber or chloroprene rubber that has very good high temperature resistance.
The carcass of this product has very adhesion after the special treatment of coating and shaping. Under normal working temperature of below 180C, the belt is low in elongation, excellent in anti-abrasion and can bear 250 C ( In the cooling condition, 300C~ 600C) high temperature for a short time. The belt is suitable for use in cement, metallurgical and steel industry.
1.Heat resistant cover resists cracking and hardening.
2.High temperature resistance to tearing and abrasion.
3.High strength carcass construction.
4.The carcass with heat-resistant material.
Difference before and after aging (IRHD )
After aged Max. Value(IRHD)
The performance rate of change reduces, %
After aged Min. Value, Mpa
Change rate of performance reduces, %
After aged Min. Value, %
Between Cover and Cloth
Cover Thickness< 1.5 mm
Cover thickness > 1.5 mm
Chemical Fiber filement fabric carcass
Longitudinal average value >, N/mm
Longitudinal Lowest Peak, N/mm
DCCD ®/ HONGXIN® RUBBER provides complete technical support to ensure the products installed in time and run safety.
The main purpose of technical support is to solve the products or technical problems which are beyond to the clients.
Clients should provide necessary assistance during the services.
Communications support: the engineers help to solve the problems by various means of communication, main including phone answer, video or graphic by email.
Field support: onsite install and guide service is available according to clients requirement
For clients requirements, we will react quickly with 24 hours, no more than 48 hours at the latest.
Give solutions by telephone
The solution was obtained by experiment, then notify the clients.